440C是马氏体不锈钢的代表钢种，可经热处理而达到高硬度（所有不锈钢、耐热钢中最高）。通常用于制造轴承、刀具，或腐蚀条件下要求高负荷、高耐磨的塑料模具。
美标中440不锈钢有四个牌号。440A、440B、440C的含碳量依次升高；440F（ASTM A582）则在440C的基础上加大S的含量，是一种易切削钢种。国内对应的牌号有9Cr18、9Cr18Mo等。
牌号对照
| 美国 | ASTM | 440A | 440B | 440C | 440F |
| 美国 | UNS | S44002 | S44003 | S44004 | S44020 |
| 日国 | JIS | SUS 440A | SUS 440B | SUS 440C | SUS 440F |
| 德国 | DIN | 1.4109 | 1.4122 | 1.4125 | — |
| 中国 | GB | 7Cr17 | 8Cr17 | 11Cr17 9Cr18Mo |
Y11Cr17 |
成分规范
| 牌号 | 440A | 440B | 440C | 440F | 9Cr18 | 9Cr18Mo |
| C | 0.6 0.75 |
0.75 0.95 |
0.95 1.2 |
0.95 1.2 |
0.9 1 |
0.95 1.1 |
| Si | ≤1.00 | ≤1.00 | ≤1.00 | ≤1.00 | ≤0.80 | ≤0.80 |
| Mn | ≤1.00 | ≤1.00 | ≤1.00 | ≤1.25 | ≤0.80 | ≤0.80 |
| P | ≤0.040 | ≤0.040 | ≤0.040 | ≤0.060 | ≤0.040 | ≤0.040 |
| S | ≤0.030 | ≤0.030 | ≤0.030 | ≥0.150 | ≤0.030 | ≤0.030 |
| Cr | 16 18 |
16 18 |
16 18 |
16 18 |
17 19 |
16 18 |
| Mo | ≤0.75 | ≤0.75 | ≤0.75 | — | — | 0.4 0.7 |
| Ni | (≤0.50) | (≤0.50) | (≤0.50) | (≤0.50) | (≤0.60) | (≤0.60) |
| Cu | (≤0.50) | (≤0.50) | (≤0.50) | (≤0.60) | — | — |
注：括号内数值表示允许加入，并非强制要求。
硬度
| 牌号 | 硬度 | 硬度 |
| 退火态（HB） | 经过热处理（HRC） | |
| 440A | ≤255 | ≥54 |
| 440B | ≤255 | ≥56 |
| 440C | ≤269 | ≥58 |
| 440F | ≤269 | ≥58 |